Namuhla, ezinhlelweni eziningi i-Alnico ithathelwe indawo yi-Neodymium noma uzibuthe we-Samarium Cobalt. Kodwa-ke, impahla yayo efana nokuzinza kwezinga lokushisa kanye namazinga okushisa aphakeme kakhulu asebenza kakhulu enza omagnethi be-Alnico babaluleke kakhulu ezimakethe zezicelo ezithile.
1. Inkundla kazibuthe ephezulu. I-Residual induction iphakeme ku-11000 Gauss icishe ifane nozibuthe we-Sm2Co17, bese ingakhiqiza insimu ephakeme kazibuthe nxazonke.
2. Izinga lokushisa eliphezulu lokusebenza. Izinga lokushisa layo eliphezulu lokusebenza lingaba phezulu lifike ku-550⁰C.
3. Ukuqina kwezinga lokushisa eliphezulu: Ozibuthe be-Alnico banama-coefficients okushisa angcono kakhulu anoma iyiphi into kazibuthe. Ozibuthe be-Alnico kufanele bathathwe njengenketho engcono kakhulu ekusetshenzisweni kokushisa okuphezulu kakhulu.
4. Ukumelana nokugqwala okuhle kakhulu. Ozibuthe be-Alnico abajwayele ukugqwala futhi bavame ukusetshenziswa ngaphandle kokuvikelwa kwendawo
1. Kulula ukususa uzibuthe: Amandla ayo aphezulu okuphoqeleka aphansi we-Hcb angaphansi kuka-2 kOe bese kuba lula ukukhipha uzibuthe endaweni ethile ephansi ye-demagnetizing, noma ingaphathwa ngokunakekela.
2. Iqinile futhi ishwabene. Ijwayele ukuqhekeka nokuqhekeka.
1. Njengoba ukuphoqelelwa kozibuthe be-Alnico kuphansi, isilinganiso sobude nobubanzi kufanele sibe ngu-5:1 noma ngaphezulu ukuze uthole iphoyinti lokusebenza elihle le-Alnico.
2. Njengoba izibuthe ze-Alnico zikhishwa kalula uzibuthe ngokuphatha ngokunganaki, kunconywa ukwenza i-magnetizing ngemva kokuhlanganiswa.
3. Ozibuthe be-Alnico banikeza ukuzinza okuvelele kwezinga lokushisa. Okukhiphayo okuvela kuzibuthe ze-Alnico kuyahluka kancane ngokushintsha kwezinga lokushisa, okuyenza ibe ukukhetha okuhle kwezinhlelo zokusebenza ezizwelayo kumazinga okushisa, njengezokwelapha nezempi.
Nakanjani asibona abakhi bezibuthe be-Alnico, kodwa singochwepheshe bezinhlobo kazibuthe zozibuthe baphakade okuhlanganisa ne-Alnico. Ngaphezu kwalokho, ozibuthe bethu bomhlaba abayivelakancane abakhiqizwe kanye nenhlanganisela kazibuthe kuzokwenza amakhasimende abe nokuthenga okukodwa kwemikhiqizo kazibuthe evela kithi kalula.
| I-Cast / Sintered | Ibanga | I-MMPA efanayo | Br | Hcb | (BH) ubuningi | Ukuminyana | α(Br) | TC | TW |
| mT | KA/m | KJ/m3 | g/cm3 | %/ºC | ºC | ºC | |||
| Abalingisi | LNG37 | I-Alnico5 | 1200 | 48 | 37 | 7.3 | -0.02 | 850 | 550 |
| I-LNG40 | 1230 | 48 | 40 | 7.3 | -0.02 | 850 | 550 | ||
| I-LNG44 | 1250 | 52 | 44 | 7.3 | -0.02 | 850 | 550 | ||
| I-LNG52 | I-Alnico5DG | 1300 | 56 | 52 | 7.3 | -0.02 | 850 | 550 | |
| I-LNG60 | I-Alnico5-7 | 1330 | 60 | 60 | 7.3 | -0.02 | 850 | 550 | |
| LNGT28 | I-Alnico6 | 1000 | 56 | 28 | 7.3 | -0.02 | 850 | 550 | |
| I-LNGT36J | I-Alnico8HC | 700 | 140 | 36 | 7.3 | -0.02 | 850 | 550 | |
| I-LNGT18 | I-Alnico8 | 580 | 80 | 18 | 7.3 | -0.02 | 850 | 550 | |
| I-LNGT38 | 800 | 110 | 38 | 7.3 | -0.02 | 850 | 550 | ||
| I-LNGT44 | 850 | 115 | 44 | 7.3 | -0.02 | 850 | 550 | ||
| I-LNGT60 | I-Alnico9 | 900 | 110 | 60 | 7.3 | -0.02 | 850 | 550 | |
| I-LNGT72 | 1050 | 112 | 72 | 7.3 | -0.02 | 850 | 550 | ||
| I-Sintered | I-SLNGT18 | I-Alnico7 | 600 | 90 | 18 | 7.0 | -0.02 | 850 | 450 |
| I-SLNG34 | I-Alnico5 | 1200 | 48 | 34 | 7.0 | -0.02 | 850 | 450 | |
| I-SLNGT28 | I-Alnico6 | 1050 | 56 | 28 | 7.0 | -0.02 | 850 | 450 | |
| I-SLNGT38 | I-Alnico8 | 800 | 110 | 38 | 7.0 | -0.02 | 850 | 450 | |
| I-SLNGT42 | 850 | 120 | 42 | 7.0 | -0.02 | 850 | 450 | ||
| I-SLNGT33J | I-Alnico8HC | 700 | 140 | 33 | 7.0 | -0.02 | 850 | 450 |
| Izici | I-Reversible Temperature Coefficient, α(Br) | I-Reversible Temperature Coefficient, β(Hcj) | I-Curie Temperature | I-Max Operating Temperature | Ukuminyana | Ukuqina, Vickers | Ukungazweli Kagesi | I-Coefficient of Thermal Expansion | Amandla Okuqina | Amandla Wokucindezela |
| Iyunithi | %/ºC | %/ºC | ºC | ºC | g/cm3 | Hv | μΩ • m | 10-6/ºC | Mpa | Mpa |
| Inani | -0.02 | -0.03~+0.03 | 750-850 | 450 noma 550 | 6.8-7.3 | 520-700 | 0.45~0,55 | 11-12 | 80-300 | 300-400 |